Mesoporous silica manufactured in the presence of water-soluble odso

ABSTRACT

Mesoporous silica is disclosed possessing a two-dimensional, hexagonal, through-hole structure with a space group p6mm, that is formed using one or more water-soluble oxidized disulfide oil (ODSO) compounds during the synthesis to impart distinct characteristics including an increased percentage of silanol groups.

RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent applicationSer. No. 17/347,125 filed Jun. 14, 2021, the contents of which are isincorporated herein by reference.

BACKGROUND OF THE INVENTION Field of the Invention

The present invention relates to mesoporous silica.

Description of Related Art

Zeolites are microporous aluminosilicate materials (pores typically upto 2 nm) that are heavily used in industry as catalysts or catalyst basematerials (catalytic cracking of hydrocarbons and as components incatalytic convertors), adsorbents (drying agents) and ion exchangematerials (water softening). Whereas zeolites have found great utilityin their ability to select between small molecules and differentcations, mesoporous solids (pores between 2 nm and 50 nm) offerpossibilities for applications for species up to an order of magnitudelarger in dimensions such as nanoparticles and enzymes. Thecomparatively bulky nature of such species hinders diffusion through themicroporous zeolite network, and thus, a larger porous system isrequired to effectively perform an analogous molecular sieving actionfor the larger species.

The field of mesoporous materials primarily stems from zeolite researchundertaken during the 1990s when researchers were pursuing large porezeolite analogues for heavy hydrocarbon conversion (Ordered mesoporousmolecular sieves synthesized by a liquid-crystal template mechanism. C.T. Kresge, M. E. Leonowicz, W. J. Roth, J. C. Vartuli and J. S. Beck,Nature, 1992,359,710; A new family of mesoporous molecular sievesprepared with liquid crystal templates, J. S. Beck, J. C. Vartuli, W. J.Roth, M. E. Leonowicz, C. T. Kresge, K. D. Schmitt, C. T. W. Chu, D. H.Olson, E. W. Sheppard, S. B. McCullen, J. B. Higgins and J. L.Schlenker, J. Am. Chem. Soc., 1992, 114, 10834). Since numeroussynthetic architectures were crystallized around structure directingagents or templates, which, upon removal, renders the material porous,the rationale was that larger templates or aggregations of moleculescould act as a mold. Mesoporous silica was realized in 1992, with MCM-41(Mobil Composition of Matter) templated using amphiphilic surfactantaggregations in a sol-gel synthesis, namely using CTAB(cetyltrimethylammonium bromide).

Mesoporous silicas are amorphous; however, it is the pores that possesslong-range order with a periodically aligned pore structure and uniformpore sizes on the mesoscale. Mesoporous silicas offer high surface areasand can be used as host materials to introduce additional functionalityfor a diverse range of applications such as adsorption, separation,catalysis, drug delivery and energy conversion and storage.

“Soft” templates can be used for the synthesis of mesoporous silica, forexample CTAB and amphiphilic block copolymers. A common reagent for thelatter block copolymer is Pluronic P123 (BASF). The SBA-series (SantaBarbara) of mesoporous silicas (Dongyuan Zhao, Qisheng Huo, JianglinFeng, Bradley F Chmelka, Galen D Stucky, J. Am. Chem. Soc., 1998, 120,6024) further opened the field of mesoporous silicas with larger poresby utilizing such block copolymer templates in the syntheses ofmesoporous silicas. This “soft” templating approach allows for themesopore structure, shape and pore size to be designed throughcontrolling the synthesis conditions and the nature of the templateused. Pluronic P123 used for production of SBA-15 mesoporous silica is atriblock copolymer of ethylene oxide/propylene oxide/ethylene oxidehaving the composition (EO₂₀PO₇₀EO₂₀).

Surfactants, used as the templates for mesoporous silicas, and deemedamphiphilic molecules, possess a hydrophilic head group and ahydrophobic tail, and can be classified into various types depending ontheir constituent groups:

-   -   i) cationic whereby the hydrophobic head groups are        amine/quaternary ammonium cations as in CTAB,    -   ii) anionic constituting for example carboxylic head groups,    -   iii) non-ionic having polyether/polyhydroxyl polar groups, or    -   iv) zwitterionic containing two charged head groups of opposite        charge. The hydrophobic section tends to be long alkyl chains.

At low concentrations surfactants exist as discrete entities. However,at higher concentrations, that is, above the critical micelleconcentration (CMC), micelles are formed. The hydrophobic interactionsin the system comprising the surfactant can alter the packing shape ofthe surfactants into spherical, prolate or cylindrical micelles, whichcan thereafter form thermodynamically stable two dimensional or threedimensional liquid crystalline phases of ordered mesostructures. Thesurfactant geometry influences the mesophase formed, from cubic tolamellar.

The sol-gel route is typically used to synthesize SBA-15 and involves atwo-step process: a hydrolysis step followed by a condensation step.

Hydrolysis: Si(OR)₄+H₂O→HO—Si(OR)₃+ROH  (1)

Condensation: 2(OR)₃SiOH→(OR)₃Si—O—Si(OH)₃+H₂O  (2)

where R is an alkyl.

Mesoporous silica can be functionalized by post-synthetic grafting of,for example organosiloxanes. First the mesoporous silica need to berendered porous by removing the surfactant from the pores. This istypically done by calcining the material to leave the porous inorganicsilica framework. However, calcining mesoporous silica further condensesthe framework to form additional siloxane bridges (a higher degree of Q⁴silica). Post synthetic modification by organosiloxane grafting can onlyoccur where there are silanol groups as these act as anchors for theorganosiloxane, thus Q³, Q², Q¹ or Q⁰ silica must be present as Q⁴silica are fully condensed to form a rigid framework. Since calcinationcondenses the framework there is a decreased volume of silanol groupsavailable for organic modification silylation and so that silanol groupshave to be replenished if a high surface coverage of functional groupsis required. This can be achieved by rehydrating the surface.

Within a typical refinery, there are by-product streams that must beprocessed in other process units or otherwise disposed of. The mercaptanoxidation process, commonly referred to as the MEROX process, has longbeen employed for the removal of the generally foul smelling mercaptansfound in many hydrocarbon streams and was introduced in the refiningindustry over fifty years ago. Because of regulatory requirements forthe reduction of the sulfur content of fuels for environmental reasons,refineries have been, and continue to be faced with the disposal oflarge volumes of sulfur-containing by-products. Disulfide oil (DSO)compounds are produced as a by-product of mercaptan oxidation processes,known as a MEROX process, in which the mercaptans are removed from anyof a variety of petroleum streams including liquefied petroleum gas,naphtha, and other hydrocarbon fractions. It is commonly referred to asa ‘sweetening process’ because it removes the sour or foul smellingmercaptans present in crude petroleum. The term “DSO” is used forconvenience in this description and in the claims, and will beunderstood to include the mixture of disulfide oils produced asby-products of the mercaptan oxidation process. Examples of DSO includedimethyldisulfide, diethyldisulfide, and methylethyldisulfide.

The by-product DSO compounds produced by the MEROX unit can be processedand/or disposed of during the operation of various other refinery units.For example, DSO can be added to the fuel oil pool at the expense of aresulting higher sulfur content of the pool. DSO can be processed in ahydrotreating/hydrocracking unit at the expense of higher hydrogenconsumption. DSO also has an unpleasant foul or sour smell. Therefore,it is known that problems exist in the handling of DSO.

Commonly owned U.S. Pat. No. 10,807,947 which is incorporated byreference herein in its entirety discloses a controlled catalyticoxidation of MEROX process by-products DSO. The resulting oxidizedmaterial is referred to as oxidized disulfide oil (ODSO). As disclosedin 10,807,947, the by-product DSO compounds from the mercaptan oxidationprocess can be oxidized, preferably in the presence of a catalyst. Theoxidation reaction products constitute an abundant source of ODSOcompounds, sulfoxides, sulfonates, sulfinates and sulfones. The oxidantcan be a liquid peroxide selected from the group consisting of alkylhydroperoxides, aryl hydroperoxides, dialkyl peroxides, diarylperoxides, peresters and hydrogen peroxide. The oxidant can also be agas, including air, oxygen, ozone and oxides of nitrogen. The catalystcan be a homogeneous compound that is a transition metal containing anactive species selected from the group consisting of Mo (VI), W (VI), V(V), Ti (IV), and combinations thereof.

ODSO compounds are disclosed in U.S. Pat. No. 10,781,168 as a solvent(in general), in U.S. Pat. No. 10,793,782 as an aromatics extractionsolvent, and in U.S. Pat. No. 10,927,318 as a lubricity additive, all ofwhich are incorporated by reference herein in their entireties. In theevent that a refiner has produced or has on hand an amount of DSOcompounds that is in excess of foreseeable needs for these or otheruses, the refiner may wish to dispose of the DSO compounds in order toclear a storage vessel and/or eliminate the product from inventory fortax reasons.

Thus, there is a clear and long-standing need to provide an efficientand economical process for the treatment of the large volumes of DSOby-products and their derivatives to effect and modify their propertiesin order to facilitate and simplify their environmentally acceptabledisposal, and to utilize the modified products in an economically andenvironmentally friendly manner, and thereby enhance the value of thisclass of by-products to the refiner.

Despite the known methods that exist for manufacturing SBA-15 mesoporoussilica, there remains a need in the art for improved methods to produceSBA-15 mesoporous silica and modified mesoporous silica materials.

SUMMARY

Methods of synthesis of mesoporous silica are disclosed. The mesoporoussilica synthesized herein, like SBA-15, possesses a two-dimensional,hexagonal, through-hole structure with a space group p6mm.

In one embodiment, the method comprises mixing in an aqueous mediumunder conditions conducive to promote hydrolysis reactions effectivequantities of a surfactant as a soft template material to influence asilica mesoporous structure, one or more water-soluble ODSO compounds asan acidity modifier, and a silica source. The mixture is then heatedunder conditions and for a time effective conducive to promotecondensation reactions and to form mesoporous silica as a precipitatesuspended in a supernatant as an intermediate suspension. The mesoporoussilica is recovered from the intermediate suspension. In certainembodiments the recovered mesoporous silica is treated to remove thesurfactant, for example, by thermal treatment to realize the calcinedmesoporous silica material.

In another embodiment, the method comprises mixing in an aqueous mediumeffective quantities of one or more water-soluble ODSO compounds as anacidity modifier and a surfactant as a soft template material toinfluence a silica mesoporous structure to form a first mixture; mixingan effective quantity of a silica source with the first mixture underconditions conducive to promote hydrolysis reactions and form a secondmixture; heating the second mixture under conditions and for a timeeffective conducive to promote condensation reactions and to formmesoporous silica as a precipitate suspended in a supernatant as anintermediate suspension, and recovering the mesoporous silica from theintermediate suspension. In certain embodiments the recovered mesoporoussilica is treated to remove the surfactant, for example, by thermaltreatment to realize the calcined mesoporous silica material.

Still other aspects, embodiments, and advantages of these exemplaryaspects and embodiments, are discussed in detail below. Moreover, it isto be understood that both the foregoing information and the followingdetailed description are merely illustrative examples of various aspectsand embodiments, and are intended to provide an overview or frameworkfor understanding the nature and character of the claimed aspects andembodiments. The accompanying drawings are included to provideillustration and a further understanding of the various aspects andembodiments, and are incorporated in and constitute a part of thisspecification. The drawings, together with the remainder of thespecification, serve to explain principles and operations of thedescribed and claimed aspects and embodiments.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will be described in further detail below and withreference to the attached drawings in which the same or similar elementsare referred to by the same number, and where:

FIG. 1A shows X-ray diffraction patterns of conventional SBA-15 andmesoporous silica synthesized in the presence of ODSO (MS-ODSO);

FIG. 1B is an enlarged section of the patters shown in FIG. 1 ;

FIG. 2 shows scanning electron microscopy images of conventional SBA-15and MS-ODSO;

FIG. 3 is a graph of Q⁴, Q³ and Q² populations of conventional SBA-15and MS-ODSO, determined from ²⁹Si nuclear magnetic resonancespectroscopy, and associated structural formulae of Q⁴ siloxanes, Q³silanols and Q² silanols; and

FIG. 4 presents graphs of thermogravimetric and differentialthermogravimetric (DTG) data of conventional SBA-15 and MS-ODSO.

DETAILED DESCRIPTION

Described herein are methods of manufacture of mesoporous silica havinghexagonal p6mm symmetry, similar to SBA-15 mesoporous silicas, and areuseful as a catalysts or catalyst base materials. An effective quantityof one or more water-soluble ODSO compounds are used during synthesis,as described herein, to impart distinct characteristics. The processherein uses the ODSO as a substitute for, or in combination with, anacid that is conventionally used in the production of SBA-15 mesoporoussilica, such as hydrochloric acid. As used herein, the as-producedmesoporous silica is sometimes referred to as “MS-ODSO.” It isunderstood that this notation shall be applicable for the so-producedmesoporous silica in its condition prior to treatment to remove thesurfactant, such as thermal treatment or solvent extraction, or in itstreated state.

A sol-gel synthesis method comprises mixing, in an aqueous medium, asilica source, a surfactant, and an effective amount of one or more ODSOcompounds, wherein the ODSO can be used as a replacement for anotheracid or in combination therewith. The mixture is heated under conditionsand for a time effective to form the mesoporous silica asthermodynamically stable two dimensional or three dimensional liquidcrystalline phases of ordered mesostructures, as a precipitate suspendedin a supernatant. The mesoporous silica is recovered from thisintermediate suspension of the precipitate in the supernatant, forexample by filtration, washing and drying.

A porous material is obtained by treating recovered precipitate toremove the surfactant, for example by thermal treatment and/or solventextraction. For example, thermal treatment can include calcination at asuitable temperature, temperature ramp rate and for a suitable period oftime at to realize MS-ODSO. Alternatively, a solvent with a Hildebrandsolubility factor more than 18, including but not limited to ethanol(Hildebrand solubility factor of 26.2), can be used in a solventextraction process, which is effective to remove the surfactant and anyremaining content from the TEMs. In certain embodiments, a solventextraction process is suitable to realize an increase in silanol groupswhen compared with calcination.

In the process herein, one or more water-soluble ODSO compounds are usedin the synthesis of mesoporous silica, including those that containthree or more oxygen atoms, to facilitate synthesis using water as themedium. The one or more ODSO compounds can include compounds of thegeneral formulae R—SOO—SO—R′, R—SOO—SOO—R′, R—SO—SOO—OH, R—SOO—SOO—OH,R—SO—SO—OH, R—SOO—SO—OH, and mixtures thereof, where R and R′ can be thesame or different and are alkyl groups comprising 1-10 carbon atoms. Incertain embodiments, the R and R′ are methyl and/or ethyl groups. Theone or more ODSO compounds used in the synthesis of MS-ODSO generallyinclude ODSO compounds having 3 or more oxygen atoms. In certainembodiments, one or more ODSO compounds used in the synthesis of MS-ODSOinclude ODSO compounds having 1 to 20 carbon atoms. In certainembodiments, one or more ODSO compounds used in the synthesis of MS-ODSOinclude ODSO compounds having an average density greater than about 1.0g/cc. In certain embodiments, one or more ODSO compounds used in thesynthesis of MS-ODSO include ODSO compounds having an average boilingpoint greater than about 80° C.

In certain embodiments ODSO compounds used in the synthesis of MS-ODSOcomprise all or a portion of water-soluble ODSO compounds contained inan oxidation effluent stream that is obtained by oxidation of DSOcompounds from a MEROX process, as disclosed in U.S. Pat. Nos.10,807,947 and 10,781,168 and as incorporated herein by reference above.Table 1 identifies certain water-soluble ODSO compounds that are formedby oxidation of DSO obtained from MEROX by-products.

TABLE 1 ODSO Name Formula Structure Examples Dialkyl-sulfonesulfoxide Or1,2-alkyl-alkyl-disulfane 1,1,2-trioxide (R-SOO-SO-R’)

Dialkyl-disulfone Or 1,2 alkyl-alkyl-disulfane 1,1,2,2-tetraoxide(R-SOO-SOO-R’)

Alkyl-sulfoxidesulfonate (R-SO-SOO-OH)

Alkyl-sulfonesulfonate (R-SOO-SOO-OH)

Alkyl-sulfoxidesulfinate (R-SO-SO-OH)

Alkyl-sulfonesulfinate (R-SOO-SO-OH)

R and R’ can be the same or different alkyl groups comprising 1-10carbon atoms.

In certain embodiments, the ODSO compounds are contained in a mixturefrom oxidation of DSO compounds, comprising alkyl-sulfoxidesulfonate(R—SO—SOO—OH), alkyl-sulfonesulfonate (R—SOO—SOO—OH),alkyl-sulfoxidesulfinate (R—SO—SO—OH) and alkyl-sulfonesulfinate(R—SOO—SO—OH), for example, similar to those obtained as “Composition 2”in U.S. Pat. No. 10,781,168 as incorporated herein by reference above.

In the present process, one or more ODSO compounds are used in theSBA-15 sol-gel synthesis process to alter the properties of theas-produced mesoporous silica. By forming the mesoporous silica in thepresence of ODSO, the properties of the resulting MS-ODSO are differentthan those of SBA-15 prepared using conventional synthesis processesthat occur in the absence of such ODSO. The properties of theconventional SBA-15 and the MS-ODSO were characterized (as explained inmore detail below) after the hydrolysis and condensation reactions andprior to calcining (the “uncalcined” or “as-made” material), and aftercalcining (the “calcined” material). As compared to conventional SBA-15mesoporous silica, and as explained in the exampled herein, the MS-ODSOmaterial exhibits:

-   -   worm-like morphology;    -   increased unit cell dimensions in the as-made and calcined        MS-ODSO;    -   a higher degree of long-range ordering-in the as-made and        calcined MS-ODSO;    -   a higher degree of silanol (Si—OH) formation in the uncalcined        MS-ODSO due to a higher quantity of Q²+Q³ silica;    -   a lower degree of Q² silica in the uncalcined material;    -   a higher degree of siloxane bridges (Si—O—Si) due to a higher        quantity of Q³+Q⁴ silica in the uncalcined material, and hence        increased stability/rigidity of the mesoporous silica framework;    -   a lower degree of Q⁴ silica in the calcined material, for        instance where the MS-ODSO has in the range of about 0.1-50,        5-50, 0.1-35 or 5-35% less Q⁴ silica as compared to conventional        SBA-15; and    -   an increased percentage of silanol groups, which is a function        of the Q²+Q³ silica, in the calcined material, for instance        where the MS-ODSO has in the range of about 0.1-65 or 25-65%        more silanol groups as compared to conventional SBA-15.

The lower degree of Q⁴ silica and the higher degree of Q² and Q³ silicain the calcined material, as quantified by NMR spectroscopy, results inan increase in silanol (Si—OH) groups. Silanol groups in mesoporoussilica arm commonly used to provide a site to graft additionalfunctionality to the surface of the material post-synthesis. Forexample, function siloxanes groups X—Si(OCH₃)₃ can be used to:

-   -   i) alter the surface properties of the material, for example by        making the surface more hydrophobic or hydrophilic, or    -   ii) uptake additional functionality to create advanced        functional materials, for example, uptake of magnetic        nanoparticles for improved medical imaging such as magnetic        resonance imaging, graft catalytic complexes for catalysis,        immobilization of enzymes, and uptake of active pharmaceutical        ingredients for controlled release of drugs.

At low concentrations surfactants exist as discrete entities, however,at higher concentrations (above the CMC) micelles are formed. Thehydrophobic interactions in the system comprising the surfactant canalter the packing shape of the surfactants into spherical, prolate orcylindrical micelles, which can thereafter form thermodynamically stabletwo dimensional or three dimensional liquid crystalline phases ofordered mesostructures. The surfactant geometry influences mesophaseformed, from cubic to lamellar; the geometry of the conventional SBA-15and the MS-ODSO are both hexagonal p6mm symmetry.

Aside from the addition of ODSO described herein, the sol-gel synthesisis similar to known processes, for example as mentioned in thebackground and described with respect to formulae (1) and (2). Ingeneral, a sol-gel synthesis process to realize mesoporous silica asdescribed herein starts with a colloidal aqueous solution of a (i)silica source, (ii) an acid medium, and (iii) a surfactant as a softtemplate material to influence a silica mesoporous structure. In theconventional SBA-15 synthesis processes, the acid medium is a separateacid; in the process herein, the acidity of the acid medium is attachedby the ODSO compounds, directly and/or based on hydrolysis in the watermedium to form acids.

Surfactants used as the templates for large pore mesoporous silicas arecopolymers, block copolymers or triblock copolymers, and are generallyamphiphilic molecules. The amphiphilic molecules can be cationic,anionic, non-ionic and/or zwitterionic. In certain embodiments aneffective surfactant comprises a non-ionic surfactant. In certainembodiments an effective surfactant comprises a triblock copolymer ofethylene oxide/propylene oxide/ethylene oxide. For example, a suitabletriblock copolymer of ethylene oxide/propylene oxide/ethylene oxide hasthe general composition EO₂₀PO₇₀EO₂₀, and is commercially availableunder the tradename Pluronic P123 (BASF), and is useful for thesynthesis of SBA-15.

The mesoporous silica formation including the surfactant isacid-catalyzed, for example to realize a pH level less than about 3, 2or 1. In conventional SBA-15 synthesis, this is by the addition of aneffective amount of hydrochloric acid (HCl), sulfuric acid (H₂SO₄),hydrobromic acid (HBr), phosphoric acid (H₃PO₄) or nitric acid (HNO₃);typically in reported SBA-15 synthesis methods the acid is HCl. In theprocess herein to produce MS-ODSO, all or a portion of the requisiteacidity is contributed by the ODSO. For example, a conventional acidsource as noted above can be used in an amount that is 0-99, 0-50, 0-25,5-99, 5-50 or 5-25 molar % of the amount required to attain a pH in arange of about 1-3 in the absence of ODSO. In certain embodiments, theonly acidity modifier is the ODSO.

The silica source can comprise one or more of tetraethyl orthosilicate(TEOS), tetramethyl orthosilicate (TMOS), tetrapropyl orthosilicate(TPOS), tetrabutyl orthosilicate (TBOS) or sodium (meta)silicate.

In the process herein, the ratios of silica source the surfactant andwater include those that are effective for producing SBA-15 mesoporoussilica, including for example surfactant in the range of about 1-5, 1-3,2-5, 2-3 or about 2.5 wt % of the total sol-gel composition. As notedherein, the acidity modifier, which is ODSO alone or in combination withanother acid source, is added at an effective quantity to attain a pHlevel of less than or equal to about 3, 2 or 1.

In the synthesis steps for producing MS-ODSO, the sequence of adding thecomponents is described above, but can be varied. In certainembodiments, the surfactant, water and the acidity modifier (ODSO aloneor in combination with another acid) are formed into a solution, towhich the silica is then added. In other embodiments, the ODSO can beadded with the silica source.

Suitable conditions for the mixing steps described herein to produce theaqueous mixture of silica, surfactant and ODSO (and optionally anotheracidity modifier) are similar to those used in conventional SBA-15synthesis, and can be, for instance, in the range of about 20-65 or20-50° C., and at atmospheric pressure. The mixing time before silicaaddition is generally dependent on the time that it takes for thesurfactant and the ODSO to dissolve, and thereafter the silica is addedand mixed until fully dissolved and in certain embodiments mixed for anadditional 0-24 or 0-4 hours after it is fully dissolved.

The hydrolysis reactions occur at temperature and pressure conditionssimilar to those used in conventional SBA-15 synthesis, for instanceabout 20-65 or 35-65° C. and at atmospheric or autogenous pressure, andfor a time period of about 10 minutes to 24 hours or 4-24 hours. Also,condensation reactions occur at temperature and pressure conditionssimilar to those used in conventional SBA-15 synthesis, for instanceabout 80-120, 90-120, 80-110 or 90-110° C. and at atmospheric orautogenous pressure, and for a time period of about 1-4 or 1-2.5 days.

The temperature and pressure conditions, and residence time, for thewashing and filtration steps to recover precipitate from the supernatantthat is used for producing SBA-15 mesoporous silicas and the novelmesoporous silicas herein are in the range of about: 20-80° C., atatmospheric pressure or vacuum pressure (for instance, up to about 33,135 or 160 millibars absolute), and can occur until the pH of thefiltrate approaches 7. The wash can be, for example, using wash water attwice the volume of the sol-gel. The wash can be until foam (residualsurfactant) is significantly reduced. Filtration is accomplished, forinstance, using known techniques such as centrifugation, gravity, vacuumfiltration, filter press, or rotary drums.

The temperature and time for calcination to produce MS-ODSO herein canbe in the range of about: 215-600 or 450-600° C., for about 4-24, 4-16,8-24 or 8-16 hours, and a ramp rate of about 1-10 or 1-5° C. per minute.

EXAMPLES Comparative Example

1.59 g of Pluronic P123 (mw_(av) 5750) was dissolved in 55.24 g waterand 5.16 g HCl (37 wt. %) at 40° C. Once dissolved 3.3 g tetraethylorthosilicate (99 wt. %) was added to the solution and the system wasfurther stirred at 40° C. for 24 hours for the hydrolysis reaction toproceed. The molar ratio of these components can be expressed as:

1SiO₂:0.018P123:3.3HCl:208H₂O.

The mixture was transferred to a Teflon-lined autoclave and the systemisolated. The mixture was subjected to a temperature of 100° C. for 48hours for the condensation reaction to proceed. After the desired timethe autoclave was cooled and the product filtered under vacuum beforewashing with water. The resulting powder was dried at 100° C. to yieldthe as-made product. The as-made product was calcined at 550° C. (1°C./min) for 8 hours to yield the calcined SBA-15 mesoporous silicamaterial.

Example

1.59 g of Pluronic P123 (mw_(av) 5750) was dissolved in 55.24 g waterand 5.16 g water-soluble ODSO at 40° C. The ODSO used in this exampleare those obtained as “Composition 2” in U.S. Pat. No. 10,781,168,incorporated herein by reference above. Once dissolved 3.3 g tetraethylorthosilicate (99 wt. %) was added to the solution and stirring wascontinued at 40° C. for 24 hours for the hydrolysis reaction to proceed.The molar ratio of these components, including ODSO* instead of HCl asin the comparative example, can be expressed as:

1SiO₂:0.018P123:2.2ODSO:196H₂O.

*Based on the data in the referenced U.S. Pat. No. 10,781,168, anaverage molecular weight of 151.2 can be assumed, for a molarcomposition of 2.2, relative to the other components as shown.

Thereafter, the mixture was transferred to a Teflon-lined autoclave andthe system isolated. The mixture was subjected to a temperature of 100°C. for 48 hours for the condensation reaction to proceed. After thedesired time the autoclave was cooled and the product filtered undervacuum before washing with water. The resulting powder was dried at 100°C. to yield the as-made MS-ODSO material (also referred to herein as theuncalcined MS-ODSO material). The as-made material was calcined at 550°C. (1° C./min) for 8 hours to yield the calcined MS-ODSO material.

FIG. 1A shows X-ray diffraction patterns of the calcined SBA-15mesoporous silica material of the comparative example and the MS-ODSOmaterial of the Example synthesized in the presence of ODSO. FIG. 1Bshows an enlarged section of the graph of FIG. 1A between the 2θ angles1° and 3°. X-ray diffraction is carried out with an X-ray source of CuKα radiation (k=1.5406 Å) and the graph is presented in a known formatof scattering, the 2θ angles, on the x-axis, plotted against intensity,measured in arbitrary units, on the y-axis. From FIG. 1B, it is observedthat the long-range order is enhanced in the MS-ODSO compared toconventional SBA-15. The tertiary 2 1 and 3 0 peak reflections are moreenhanced in the MS-ODSO as compared to the conventional SBA-15.

Table 2 presents unit cell dimensions of the comparative and the MS-ODSOmaterials. The MS-ODSO has its diffraction pattern shifted to lower 2θangles, which is indicative of larger unit cell dimensions.

TABLE 2 Material 2θ (º) Interplanar spacing, d₁₀ (Å) Unit cell, a₁₀ (Å)*SBA-15 0.93  95 110 SBA-15 ODSO 0.86 103 119 *Hexagonal latticeparameter; a = √(4/3) d₁₀ ².

FIG. 2 presents scanning electron micrographs of conventional SBA-15material and MS-ODSO material. Both show worm-like morphology.

FIG. 3 shows ²⁹Si NMR data and specifically the Q⁴, Q³ and Q²populations of conventional SBA-15 mesoporous silica material andMS-ODSO mesoporous silica material synthesized in the presence of ODSO.There are clear differences between the framework composition betweenthe two samples. Samples were packed into 4 mm solid-state NMR samplerotors. Magic angle spinning (MAS) experiments were performed on aVarian 500 MHz NMR spectrometer using a 4 mm HX probe. ²⁹Si MASexperiments were performed at a spinning frequency of 10 kHz. Theobtained spectra were processed in MestreNova. Line fitting wasperformed on the spectra for peaks at approximate chemical shifts of−110 ppm (Q⁴), −100 ppm (Q³) and −90 ppm (Q²). The area under thedeconvoluted peaks were used to determine the percentage of Q^(n)functionality present via the following equation:

% Q ^(n)=Area under deconvoluted Q ^(n) peak/Area under all deconvolutedpeaks  (3)

When synthesized in the presence of ODSO, the uncalcined MS-ODSOmaterial exhibits a 57% reduction in the amount of Q² silica, and anincrease in the stability/rigidity of the mesoporous silica materialframework due to the increased number of siloxane bridges (Si—O—Si) Q³and Q⁴ (up by 7%).

In the calcined MS-ODSO, there is an increase in number of silanolgroups which will allow for greater surface coverage of functionalgroups by silylation, due to a reduction in the Q⁴ silica (reduced by20%).

Based on the nitrogen adsorption isotherm data, there is an increase inthe BET surface area (based on the known BET (Brunauer, Emmett andTeller theory) for MS-ODSO relative to conventional SBA-15 by about 10%(BET of MS-ODSO=893 m²/g; BET of conventional SBA-15=811 m²/g). Thepercentage of microporous surface area to the total surface area isincreased for MS-ODSO by about 49% (MS-ODSO microporous surface area=153m²/g; conventional SBA-15 microporous surface area=103 m²/g). The totalpore volume increased in the MS-ODSO by about 18% (conventionalSBA-15=1.07 cc/g; MS-ODSO=1.26 cc/g). In addition, the pore sizes of theMS-ODSO material increases relative to the conventional SBA-15, from 6.5nm in the conventional SBA-15 to 7.8 nm in the MS-ODSO, based on thedesorption branch of the isotherm and by the BJH model (the known themethod of Barrett, Joyner, and Halenda).

FIG. 4 are plots of thermogravimetric (TG) and differentialthermogravimetric (DTG) data of conventional SBA-15 and MS-ODSOsynthesized in the presence of ODSO using a TGA Q500 instrument (TAInstruments). The TG data (upper curves in FIG. 4 ) are expressed asnormalized percentage of mass change relative to temperature, and theDTG data (lower curves in FIG. 4 ) are expressed as mass % changerelative to temperature.

The methods and compositions of the present invention have beendescribed above and in the attached drawings; however, modificationswill be apparent to those of ordinary skill in the art and the scope ofprotection for the invention is to be defined by the claims that follow.

1. Mesoporous silica having hexagonal p6mm symmetry formed by theprocess of: mixing in an aqueous medium under conditions conducive topromote hydrolysis reactions effective quantities of a surfactant as asoft template material to influence a silica mesoporous structure, oneor more water-soluble oxidized disulfide oil (ODSO) compounds as anacidity modifier, and a silica source; heating the mixture underconditions and for a time effective conducive to promote condensationreactions and to form mesoporous silica as a precipitate suspended in asupernatant as an intermediate suspension; and recovering the mesoporoussilica from the intermediate suspension.
 2. The mesoporous silica as inclaim 1, wherein the mixing comprises mixing in the aqueous medium theone or more water-soluble oxidized disulfide oil (ODSO) compounds andthe surfactant to influence a silica mesoporous structure to form afirst mixture, mixing the silica source with the first mixture underconditions conducive to promote hydrolysis reactions and form a secondmixture, and wherein heating is of the second mixture.
 3. The mesoporoussilica as in claim 1, wherein the aqueous medium is an acidic aqueousmedium comprising an acid component as an additional acidity modifier.4. The mesoporous silica as in claim 1, further comprising treating themesoporous silica to remove surfactant, wherein treating comprisessolvent extraction or thermal treatment.
 5. The mesoporous silica as inclaim 1, wherein the hydrolysis reactions occur at a temperature in therange of about 20-65° C., condensation reactions occur at a temperaturein the range of about 80-120° C., and wherein removing surfactant is bythermal treatment at a temperature in the range of about 215-600° C. 6.The mesoporous silica as in claim 1, wherein the ODSO compounds include3 or more oxygen atoms.
 7. The mesoporous silica as in claim 1, whereinthe ODSO compounds having 1 to 20 carbon atoms.
 8. The mesoporous silicaas in claim 1, wherein the ODSO compounds have an average densitygreater than about 1.0 g/cc.
 9. The mesoporous silica as in claim 1,wherein the ODSO compounds have an average boiling point greater thanabout 80° C.
 10. The mesoporous silica as in claim 1, wherein the ODSOcompounds are selected from the group consisting of (R—SOO—SO—R′),(R—SOO—SOO—R′), (R—SO—SOO—OH), (R—SOO—SOO—OH), (R—SO—SO—OH),(R—SOO—SO—OH), and mixtures thereof, where R and R′ can be the same ordifferent and are alkyl groups comprising 1-10 carbon atoms.
 11. Themesoporous silica as in claim 1, wherein the silica source is selectedfrom the group consisting of tetraethyl orthosilicate (TEOS),tetramethyl orthosilicate (TMOS), tetrapropyl orthosilicate (TPOS),tetrabutyl orthosilicate (TBOS) or sodium (meta)silicate.
 12. Themesoporous silica as in claim 1, wherein the surfactant is a non-ionicsurfactant.
 13. The mesoporous silica as in claim 1, wherein thesurfactant is a triblock copolymer of ethylene oxide/propyleneoxide/ethylene oxide.
 14. The mesoporous silica as in claim 4, whereintreating is by thermal treatment resulting in calcined mesoporous silicathat possesses 0.1-65 percent more silanol groups, as a function of Q²and Q³ silica, as compared to conventional SBA-15.
 15. The mesoporoussilica as in claim 14, wherein X-ray diffraction patterns show thetertiary 2 1 and 3 0 peak reflections that are more enhanced as comparedconventional calcined SBA-15 mesoporous silica.
 16. Mesoporous silicahaving hexagonal p6mm symmetry that possesses an increased quantity ofsilanol groups as compared to conventional SBA-15.
 17. The mesoporoussilica as in claim 16 that has been calcined and possesses 0.1-65percent more silanol groups, as a function of Q² and Q³ silica, ascompared to conventional SBA-15.
 18. The mesoporous silica as in claim17 that possesses 25-65 percent more silanol groups as compared toconventional SBA-15.
 19. The mesoporous silica as in claim 17 thatpossesses a 0.1-50 percent less Q⁴ silica as compared to conventionalSBA-15.
 20. The mesoporous silica as in claim 17, wherein X-raydiffraction patterns show the tertiary 2 1 and 3 0 peak reflections thatare more enhanced as compared conventional calcined SBA-15 mesoporoussilica.